API 5L/A106/A53 Tiyo asye san pwoblèm nan woule cho
|
Estanda |
Klas |
Konpozan chimik (%) |
Pwopriyete mekanik |
|||||
|
ASTM A53 |
C |
Si |
Mn |
P |
S |
Fòs rupture (Mpa) |
Sede fòs (Mpa) |
|
|
A |
Mwens pase oswa egal a 0.25 |
- |
Mwens pase oswa egal a 0.95 |
Mwens pase oswa egal a 0.05 |
Mwens pase oswa egal a 0.06 |
Pi gran pase oswa egal a 330 |
Pi gran pase oswa egal a 205 |
|
|
B |
Mwens pase oswa egal a 0.30 |
- |
Mwens pase oswa egal a 1.2 |
Mwens pase oswa egal a 0.05 |
Mwens pase oswa egal a 0.06 |
Pi gran pase oswa egal a 415 |
Pi gran pase oswa egal a 240 |
|
|
ASTM A106 |
A |
Mwens pase oswa egal a 0.30 |
Pi gran pase oswa egal a 0.10 |
0.29-1.06 |
Mwens pase oswa egal a 0.035 |
Mwens pase oswa egal a 0.035 |
Pi gran pase oswa egal a 415 |
Pi gran pase oswa egal a 240 |
|
B |
Mwens pase oswa egal a 0.35 |
Pi gran pase oswa egal a 0.10 |
0.29-1.06 |
Mwens pase oswa egal a 0.035 |
Mwens pase oswa egal a 0.035 |
Pi gran pase oswa egal a 485 |
Pi gran pase oswa egal a 275 |
|
|
ASTM A179 |
A179 |
0.06-0.18 |
- |
0.27-0.63 |
Mwens pase oswa egal a 0.035 |
Mwens pase oswa egal a 0.035 |
Pi gran pase oswa egal a 325 |
Pi gran pase oswa egal a 180 |
|
ASTM A192 |
A192 |
0.06-0.18 |
Mwens pase oswa egal a 0.25 |
0.27-0.63 |
Mwens pase oswa egal a 0.035 |
Mwens pase oswa egal a 0.035 |
Pi gran pase oswa egal a 325 |
Pi gran pase oswa egal a 180 |
|
API 5L PSL1 |
A |
0.22 |
- |
0.90 |
0.030 |
0.030 |
Pi gran pase oswa egal a 331 |
Pi gran pase oswa egal a 207 |
|
B |
0.28 |
- |
1.20 |
0.030 |
0.030 |
Pi gran pase oswa egal a 414 |
Pi gran pase oswa egal a 241 |
|
|
X42 |
0.28 |
- |
1.30 |
0.030 |
0.030 |
Pi gran pase oswa egal a 414 |
Pi gran pase oswa egal a 290 |
|
|
X46 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 434 |
Pi gran pase oswa egal a 317 |
|
|
X52 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 455 |
Pi gran pase oswa egal a 359 |
|
|
X56 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 490 |
Pi gran pase oswa egal a 386 |
|
|
X60 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 517 |
Pi gran pase oswa egal a 448 |
|
|
X65 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 531 |
Pi gran pase oswa egal a 448 |
|
|
X70 |
0.28 |
- |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 565 |
Pi gran pase oswa egal a 483 |
|
Estanda nan tiyo asye kabòn san pwoblèm
|
GB estanda |
Tiyo asye san pwoblèm pou objektif estriktirèl |
GB/T8162-2008 |
|
Tiyo asye san pwoblèm pou sèvis likid |
GB/TB8163-2008 |
|
|
Tib asye san pwoblèm pou chodyè ki ba ak mwayen |
GB/3087-1999 |
|
|
Tib asye san pwoblèm pou chodyè presyon ki wo |
GB/5310-1995 |
|
|
Tib marin san pwoblèm asye kabòn |
GB/T5312-1999 |
|
|
Tib asye san pwoblèm wo-presyon pou ekipman angrè chimik |
GB/6479-2000 |
|
|
ASTM estanda |
Nwa ak cho-tranpe zenk-kouvwi tiyo asye soude ak san pwoblèm |
ASTM A53 |
|
Asye kabòn san pwoblèm pou sèvis tanperati ki wo |
ASTM A106 |
|
|
San pwoblèm frèt-trase ba-kabòn asye echanjeur chalè ak tib kondansateur |
ASTM A179 |
|
|
Tib chofaj asye kabòn san pwoblèm pou presyon ki wo |
ASTM A192 |
|
|
San pwoblèm Mwayen-kabòn chofaj ak tib superchofaj |
ASTM A210 |
|
|
Kabòn san pwoblèm pou tib mekanik |
ASTM A519 |
|
|
API estanda |
Tiyo asye san pwoblèm pou aman |
Espesifikasyon API 5CT |
|
Tiyo asye san pwoblèm pou tiyo liy |
Espesifikasyon API 5L |
|
|
DIN estanda |
Tib asye san pwoblèm pou tanperati ki wo |
DIN 17175 |
|
Fwad trase tiyo previzyon san pwoblèm |
DN2391 |
|
|
Tib asye san alyaj sikilè san pwoblèm sijè a kondisyon espesyal |
DIN 1629 |
Tolerans nan tiyo asye kabòn san pwoblèm
|
Kalite tiyo |
Gwosè tiyo (mm) |
Tolerans |
|
Woule cho |
OD<50 |
±0.50mm |
|
OD ki pi gran oswa egal a 50 |
±1% |
|
|
WT<4 |
±12.5% |
|
|
WT 4-20 |
+15%, -12.5% |
|
|
WT>20 |
±12.5% |
|
|
Fwad trase |
OD 6-10 |
±0.20mm |
|
OD 10-30 |
±0.40mm |
|
|
OD 30-50 |
±0.45 |
|
|
OD>50 |
±1% |
|
|
WT mwens pase oswa egal a 1 |
±0.15mm |
|
|
WT 1-3 |
+15%, -10% |
|
|
WT >3 |
+12.5%, -10% |
Avantaj
API 5L/A106/A53 Seamless Steel Pipe ka detwi estrikti Distribisyon nan ingot la, rafine grenn asye a, epi elimine domaj yo nan mikrostruktur la, se konsa ke estrikti an asye se dans ak pwopriyete yo mekanik yo amelyore. Amelyorasyon sa a sitou reflete nan direksyon woule, se konsa ke asye a pa izotwòp nan yon sèten limit; Ti boul, fant ak looseness ki te fòme pandan vide kapab tou soude anba tanperati ki wo ak presyon.
Defo
- API 5L/A106/A53 tiyo asye san pwoblèm Apre woule cho, enklizyon ki pa metalik yo (sitou sulfid ak oksid, osi byen ke silikat) andedan asye a yo bourade nan fèy papye, ak fenomèn nan laminasyon (sandwich) parèt. Delaminasyon anpil vin pi mal pwopriyete yo tensile nan asye nan direksyon epesè a, epi li ka lakòz chire interlayer lè soude a kontrakte. Souch lokal la pwovoke pa kontraksyon soude souvan rive nan plizyè fwa souch la nan pwen sede, ki se pi gwo pase souch la ki te koze pa chaj.
- Estrès rezidyèl ki te koze pa refwadisman inegal. Estrès rezidyèl se estrès entèn pwòp tèt ou-ekilib nan absans fòs ekstèn. Cho-woule asye nan divès seksyon gen tankou estrès rezidyèl. Pi gwo gwosè seksyon an asye jeneral, se pi gwo estrès rezidyèl la. Malgre ke estrès rezidyèl la se ekilib pwòp tèt ou, li toujou gen yon efè sèten sou pèfòmans nan manm asye anba fòs ekstèn. Tankou deformation, estabilite, anti-fatig ak lòt aspè ka gen efè negatif.
- Pwodwi asye cho woule yo pa byen kontwole an tèm de epesè ak lajè bò. Nou abitye ak ekspansyon tèmik ak kontraksyon frèt, paske nan kòmansman an nan woule cho soti menm si longè a ak epesè yo jiska estanda, pral gen yon sèten diferans negatif apre refwadisman, ak pi laj nan lajè a kwen diferans negatif, pi epè a. epesè a, plis evidan pèfòmans lan. Se poutèt sa, pou gwo asye, lajè a bò, epesè, longè, Ang, ak liy kwen nan asye a pa ka oblije twò presi.